Changes in strength of the connection between high strength high modulus polyethylene fiber (HHPE) Dyneema SK-60 and epoxy matrix ED-20 depending on the technology of composite material (CM) microsamples manufacturing before and after impact on them high-frequency capacitance (HFC) discharge in a low pressure non-equilibrium low-temperature plasma (NLTP) have been investigated. The analysis of the effectiveness of plasma treatment at change adhesion ability of ultra high molecular polyethylene (UHMPE) fibers to the polymer binding substance. The possibility of creating composite materials based on UHMPE fibers after plasma treatment was shown.
полиэтиленовое волокно, композиционный материал, адгезионная способность, polyethylene fiber, composite material, adhesive ability
1. Sergeeva E.A. Izmenenie poverhnostnyh i fiziko-mehanicheskih svoystv aramidnyh volokon, modificirovannyh potokom plazmy vysokochastotnogo emkostnogo razryada ponizhennogo davleniya / E.A. Sergeeva, A.R. Ibatullina // Vestnik Kazanskogo tehnologicheskogo universiteta. - 2012. - №4. - S. 63-66.
2. Kudinov, V.V. Armirovannye plastiki. Chast' II. / V.V. Kudinov, N.V. Korneeva, I.K. Krylov // Tehnologiya metallov. - 2006. - № 7 - S.36 - 41.
3. Sergeeva, E.A. Vliyanie plazmy VChE-razryada na fiziko-mehanicheskie svoystva volokon i kompozicionnyh materialov / E.A. Sergeeva, I.A. Grishanova, I.Sh. Abdullin // Vestnik Kazanskogo tehnologicheskogo universiteta. - 2010. - №7. - S. 109-112.
4. Sergeeva, E.A. Vliyanie obrabotki plazmoy VCh-razryada na adgezionnuyu sposobnost' polimernyh volokon / E.A. Sergeeva, V.H. Abdullina // Mavlyutovskie chteniya: Vseross. molodezhn. nauch. konf.: sb. tr. v 5 t. Tom 2/ Ufimsk. gos. aviac. un-t. - Ufa: UGATU, 2009. - S. 150-152.
5. V.V. Kudinov, I.K. Krylov, N.V. Korneeva, V.I. Mamonov, M.V. Gerov. Ocenka fiziko-himicheskogo vzaimodeystviya mezhdu voloknom i matricey pri poluchenii kompozicionnyh materialov metodom wet-pull-out // FHOM.- 2007. - №6. - S. 68 - 72.