CVYAZ' MOLEKULYARNOGO, NADSEGMENTAL'NOGO I MORFOLOGICHESKIH UROVNEY V NANOKOMPOZITAH POLIETILEN VYSOKOY PLOTNOSTI/ORGANOGLINA
Abstract and keywords
Abstract (English):
It has been shown that the amorphous chains tightness extent, realized in crystallization process, is important factor of semicrystalline polymers structure formation. The close intercommunication of molecular, suprasegmental and morphological levels of the indicated polymers structure was found.

Keywords:
аморфно-кристаллический полимер, нанокомпозит, органоглина, структура, морфология, деформирование, semicrystalline polymer, nanocomposite, organoclay, structure, morphology, deformation
References

1. Mikitaev A.K., Kozlov G.V., Zaikov G.E. Polimernye nanokompozity: mnogoobrazie strukturnyh form i prilozheniy. M.: Nauka, 2009. - 278 s.

2. Ranade A., Nayak K., Fairbrother D., D’Souza N.A. Maleated and non-maleated polyethylene-montmorillonite layired silicate blown films: creep, dispersion and crystallinity. // Polymer. - 2005. - Vol. 46. - № 23. - P. 7323-7333.

3. Kozlov G.V., Sanditov D.S. Angarmonicheskie effekty i fiziko-mehanicheskie svoystva polimerov. Novosibirsk: Nauka, 1994. - 261 s.

4. Kozlov G.V., Novikov V.U. Klasternaya model' amorfnogo sostoyaniya polimerov. // Uspehi fizicheskih nauk. - 2001. - T. 171. - № 7. - S. 717-764.

5. Mikitaev A.K., Kozlov G.V., Dzhangurazov B.Zh., Dibirova K.S. Mehanizm usileniya nanokompozitov s amorfno-kristallicheskoy matricey na nadsegmental'nom urovne. // Novoe v polimerah i polimernyh kompozitah. - 2012. - № 3. - S. 67-71.

Login or Create
* Forgot password?