The structural (fractal) analysis of coke residue formation at composites high density polyethylene/aluminum hydroxide combustion was performed. It has been shown that aluminum hydroxide particles aggregates formation results in such situation, when the indicated particles decomposition is realized in loose surface layers of aggregates, whereas densely-packed central regions form coke residue.
композит, полиэтилен гидроксид алюминия, горение, коксовый остаток, агрегация, composite, polyethylene, aluminum hydroxide, combustion, coke residue, aggregation
1. Aseeva, R.M. Zaikov, G.E. Gorenie polimernyh materialov - M.: Nauka, 1981. - 278 s.
2. Borukaev, T.A. Hacukova, R.B. Ispol'zovanie gidroksidov metallov v kachestve antipirenov dlya polimernyh materialov. Mater. VI Mezhdunar. nauchn.-prakt. konf. «Novye polimernye kompozicionnye materialy» - Nal'chik: KBGU, 2010. - S. 126-131.
3. Kozlov, G.V. Yanovskiy, Yu.G. Karnet, Yu.N. Struktura i svoystva dispersno-napolnennyh polimernyh kompozitov: fraktal'nyy analiz - M.: Al'yanstransatom, 2008. - 363 s.
4. Mikitaev, A.K. Kozlov, G.V. Zaikov, G.E. Polimernye nanokompozity: mnogoobrazie strukturnyh form i prilozheniya - M.: Nauka, 2009. - 278 s.
5. Bobryshev, A.N. Kozomazov, V.N. Babin, L.O. Solomatov, V.I. Sinergetika kompozitnyh materialov - Lipeck: NPO ORIUS, 1994. - 154 s.
6. Witten, T.A. Meakin, P. Diffusion-limited aggregation at multiple growth sites. // Phys. Rev. B, 1983. - V. 28. - № 10. - P. 5632-5642.
7. Meakin, P. Witten, T.A. Growing interface in diffusion-limited aggregation. // Phys. Rev. A, 1983. - V.28. - № 5. - P. 2985-2988.