It has been offered the theoretical model of shear strength of autohesional contact for amorphous polymers within the frameworks of fractal analysis. It has been shown that the main factor, determining the indicated strength, is polymers macromolecular coil structure. The offered analysis allows prediction of polymer optimal structure for realization of autohesional contact with desired strength.
полимер, аутогезия, прочность, макромолекулярный клубок, диффузия, фрактальный анализ, polymer, autohesion, strength, macromolecular coil, diffusion, fractal analysis
1. Wool, R.P. Polymer Interfaces - München: Hanser Verlag, 1995. - 384 p.
2. Boiko, Yu.M. Prud’homme, R.E. Bonding at symmetric polymer/polymer interfaces below the glass transition temperature. // Macromolecules. - 1997. - V. 30. - № 12. - P. 3708-3710.
3. Schnell, R. Stamm, M. Creton, C. Direct correlation between interfacial width and adhesion in glassy polymers. // Macromolecules. - 1998. - V. 31. - № 7. - P. 2284-2292.
4. Boyko, Yu.M. Autogeziya amorfnyh polimerov i ih sovmestimyh smesey. // Mehanika kompozitnyh materialov. - 2000. - T. 36. - № 1. - S. 127-134.
5. Yah'yaeva, H.Sh. Zaikov, G.E. Deberdeev, T.R. Ulitin, N.V. Stoyanov, O.V. Kozlov, G.V. Magomedov, G.M. Nasyrov, I.I. Strukturnye osnovy mezhfaznoy adgezii (nanoadgezii) v polimernyh kompozitah. // Vestnik Kazanskogo tehnologicheskogo universiteta. - 2012. - T. 15. - № 5. - S. 68-70.
6. Vilgis, T.A. Flory theory of polymeric fractals - intersection, saturation and condensation. // Physica A. - 1988. - V. 153. - № 2. - P. 341-354.
7. Kozlov, G.V. Ovcharenko, E.N. Mikitaev, A.K. Struktura amorfnogo sostoyaniya polimerov - M.: Izd-vo RHTU im. D.I. Mendeleeva, 2009. - 392 s.
8. Kozlov, G.V. Temiraev, K.B. Shustov, G.B. Mashukov, N.I. Modeling of solid state polymer properties at the stage of synthesis: fractal analysis. // J. Appl. Polymer Sci. - 2002. - V. 85. - № 6. - P. 1137-1140.
9. Budtov, V.P. Fizicheskaya himiya rastvorov polimerov - SPb.: Himiya, 1982. - 392 s.
10. Aharoni, S.M. On entanglements of flexible and rodlike polymers. // Macromolecules. - 1983. - V. 16. - № 9. - P. 1722-1728.
11. Aharoni, S.M. Correlation between chain parameters and failure characteristics of polymers below their glass transition temperature. // Macromolecules. - 1985. - V. 18. - № 12. - P. 2624-2630.
12. Kozlov, G.V. Nafadzokova, L.H. Zaikov, G.E. Yarullin, A.F. Fizicheskie aspekty razdeleniya gazov neporistymi polimernymi membranami: fraktal'nyy analiz. // Vestnik Kazanskogo tehnologicheskogo universiteta. - 2012. - T. 15. - № 9. - S. 97-100.