The possibility of obtaining mixed olefin thermoplastic with high performance by sharing polypropylene and ethylene propylene rubber (EPDM) ) and product forming by injection molding and extrusion was shown.
смесевые термоэластопласты, литье под давлением, экструзия, прочность, модуль упругости, mixed, thermoplastic elastomers, moulding, extrusion, strength, modulus of elasticity
1. Pererabotka plastmass: spravochnoe posobie / pod red. V.A. Braginskogo. - L.: Himiya, 1985. - 296 s.
2. Bogateev G.G., Ahatova L., Abdullin I.A. Vestnik Kazanskogo tehnologicheskogo universiteta, 16, 18, 132-134 (2013).
3. Bogateev G.G., Ahatova L., Abdullin I.A. Vestnik Kazanskogo tehnologicheskogo universiteta, 16, 18, 140-142 (2013).
4. Ermakov S.N. Himicheskaya modifikaciya i smeshenie polimerov pri reakcionnoy ekstruzii / S.N. Ermakov, M.L. Kerber, T.P. Kravchenko // Plast. massy. - 2007. - № 10. - S. 25-29.
5. Mahlis F.A. Tehnologicheskiy spravochnik po rezine / F.A. Mahlis, D.L. Fedyukin. - M.: Himiya, 1989. - 400 s.
6. Kanauzova A.A. Poluchenie termoplastichnyh rezin metodom «Dinamicheskoy vulkanizacii» i ih svoystva: Tem. obzor / A.A. Kanauzova, M.A. Yumashev, A.A. Doncov. - M.: CNIITEneftehim, 1985. - 69 s.