On capillary viscometer were obtained the flow curves for major brands of polyethylene PE 80 and PE 100, used in the manufacture of pipes and fittings in the main Russian factories. The rheology constants and shear rate in the extruder's head were calculated.
реология, экструзия, расплав полимера, rheology, extrusion, polymer melt
1. Trusov K.V. Obzor rynka PE trub RUBK. Materialy Mezhdunarodnoy konferencii. Polimernye truby i fitingi. Aprel'. 2014g.
2. 2. Kimel'blat V.I. Ustoychivoe razvitie trubnoy otrasli. Plastiks №10(128) 2013. S.40-44.
3. Volkov I.V.,V.I. Kimel'blat., Musin I.N., , Vol'fson S.I. Vliyanie zatrachennoy energii smesheniya i ekstruzii na svoystva termoplastichnyh elastomernyh kompoziciy. Mehanika kompozitnyh materialov.-2000.-T.36, №5.-s.679-690.
4. Ivanov V.P., Volkov I.V., Mukmeneva N.A. Kimel'blat V.I. Izmenenie molekulyarnoy podvizhnosti v rasplave polietilena posle mehanodestrukcii v prisutstvii stabiliziruyuschih sistem. «Struktura i dinamika molekulyarnyh sistem». Sbornik statey. Vypusk XI Chast' 1.-Kazan': Kazanskiy gosudarstvennyy universitet. S.410-413. 2005.
5. Kimel'blat. V.I. Molekulyarnyy dizayn ekstruzionnyh marok PND s primeneniem special'nyh reologicheskih metodik. «Struktura i dinamika molekulyarnyh sistem». «Yal'chik 2003», Sbornik ctatey, vypusk X, chast' 1 Kazan', Moskva, Yoshkar-Ola, Ufa. S.114-117
6. Volkov I.V., Gluhov V.V., Doroginickiy M.M. Kimel'blat. V.I. Termomehanodestrukciya i stabilizaciya polietilena marki PE2NT11, Vestnik Kazanskogo tehnologicheskogo Universiteta.- Izd-vo Kazan. gos. tehnol. un-ta-2012.-t.15, №5 - S.77-79
7. Rauvendal' K. Ekstruziya polimerov/Per. s angl. pod red. A.Ya. Malkina-SPb.: Professiya, 2008.- 768 str.
8. V.I. Kimel'blat, S.I. Vol'fson, I.G.Chebotareva. Prognozirovanie ekspluatacionnyh kachestv ekstruzionnogo polietilena nizkogo davleniya po reologicheskim harakteristikam. Mehanika kompozitnyh materialov №4, 1996g, s.558-663.
9. Malkin A.Ya., Isaev A.I. Reologiya: koncepcii, metody, prilozheniya/Per s angl.-SPb.: Professiya, 2007.-560 str.
10. Briedis, I.P. Reologiya i molekulyarnoe stroenie rasplavov polietilena. 3 Relaksacionnye spektry i harakternoe vremya relaksacii / I.P. Briedis, L.A. Faytel'son / Mehanika polimerov.-1976.-№2. - C.322 - 330.
11. Malkin A.Ya., Primenenie nepreryvnogo relaksacionnogo spektra pri opisanii vyazkouprugih svoystv polimerov. // VMS, seriya A, t-48, №1, 2006, s.49-50.
12. Mikaeli V. Ekstruzionnye golovki dlya plastmass i reziny: Konstrukcii i tehnicheskie raschety / Per. s angl. Yaz. pod redakciey Volodina V.P. - SPb.: Professiya, 2007. - 427str.
13. Bortnikov V.G. Proizvodstvo izdeliy iz plasticheskih mass: Uchebnoe posobie dlya vuzov v treh tomah. Tom 2. Tehnologiya pererabotki plasticheskih mass Kazan': Izd-vo «Dom pechati».- 2002.- 399 s.
14. Osnovy tehnologii pererabotki plastmass: Uchebnik dlya vuzov / S.V. Vlasov, L.B. Kandyrin, V.N. Kuleznev i dr. - M.: Himiya, 2004. - 600s.
15. Volkov I.V., Chuprak A.I., Kimel'blat V.I., Variacii reologicheskih svoystv, kak stimul optimizacii osnovnyh parametrov svarki nagretym instrumentom vstyk Svarka i diagnostika №2 2012.- s.49-52
16. Volkov I.V., Gluhov V.V., Kamalov A.B, Kimel'blat V.I. Svyaz' pokazateley svarivaemosti PE i ego makromolekulyarnoy struktury Vestnik Kazanskogo tehnologicheskogo Universiteta.- Izd-vo Kazan. gos. tehnol. un-ta-2010.- № 10- S 600-602.
17. Volkov I.V., Gluhov V.V., Doroginickiy M.M., Kimel'blat V.I. Kontrol' izmeneniy PE 100 v processe pererabotki. Plasticheskie massy, 2012, №10, S. 58-61