Surface and mechanical properties of special fabris can be adjusted by varying the processing parameters nonequilibrium low-temperature plasma. As a result of the plasma exposure capillarity skeletal tissue increased more than 7 times, the bond strength of fabric with rubber increased by 1.5 times.
Текстильный материал, плазменная модификация, капиллярность, прочность, Textile material, plasma modification, capillarity, strength